Abstron TG3MM
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Bhansali Engineering Polymers Limited |
| Trademark: | Abstron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vxuB3N_AbstronTG3MM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Abstron TG3MM is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in the Asia-Pacific region. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20mm, injection molding 1 | 45.1 | MPa | ASTM D638 |
| Yield, 3.20mm, injection molding 2 | 49.0 | MPa | ASTM D638 |
| Flexural Modulus 3(6.40 mm, Injection Molded) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, mm, injection molding) | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20mm, injection molding | 270 | J/m | ASTM D256 |
| 23°C, 6.40mm, injection molding | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(1.8 MPa, Annealed, 6.40 mm, Injection Molded) | 90.0 | °C | ASTM D648A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | Annealed at 80°C for 2 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech A801 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
| Fenochem T 5700 | Chemiplastica, Inc. | Phenolic | Fenochem |
| LEXAN™ LUX2910 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LUVOCOM® 1-3260/schwarz | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| LNP™ VERTON™ MV008S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |