HIDEN® P603H BL
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | YUHWA Korea Petrochemical Ind. Co., Ltd. |
| Trademark: | HIDEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vwpUfg_HIDEN-P603H-BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIDEN® P603H BL is a High Density Polyethylene material. It is available in Asia Pacific. Important attributes of HIDEN® P603H BL are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 2.5 | % | Internal Method |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Environmental Stress-Cracking Resistance 1 | > 5000 | hr | ASTM D1693B |
| Carbon Black Content | 2.6 | % | ISO 6964 |
| Carbon Black Dispersion | < 3 | ISO 18553 | |
| Particle Size - Carbon Black | < 20.0 | nm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 700 | % | ASTM D638 |
| Flexural Modulus | 785 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 59.0 | °C | ASTM D648 |
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 305 TFE 5 | RTP Company | PC | RTP |
| tefabloc® TOSE 420 | Mitsubishi Chemical Performance Polymers, Inc. | SEBS | tefabloc® |
| Bynel® 4125 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| Generic ABS+PC | Generic | PC+ABS | Generic |
| Styropek® BFL 397 | Styropek S.A. de C.V. | PS (EPS) | Styropek® |