Vyncolit® BXE650/1
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vwkXVX_VyncolitBXE6501.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® BXE650/1 is an inorganic filled phenolic molding compound with excellent isotropic properties, superior dimensional stability and very high mechanical properties, even at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.98 | g/cm³ | ISO 1183 |
| Apparent Density | 0.77 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.19 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Post Shrinkage | 0.040 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.2 | % | ISO 178 |
| Tensile Modulus | 22000 | MPa | ISO 527-2 |
| Tensile Stress | 108 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.54 | % | ISO 527-2 |
| Flexural Modulus | 20000 | MPa | ISO 178 |
| Flexural Stress | 235 | MPa | ISO 178 |
| Compressive Stress | 413 | MPa | ISO 604 |
| Coefficient of Friction | |||
| Dynamic | 0.54 | ||
| Static | 0.56 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 14 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | > 250 | °C | ISO 75-2/Af |
| 8.0 MPa, not annealed | 178 | °C | ISO 75-2/Cf |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.6E-5 | cm/cm/°C | TMA |
| Lateral | 2.4E-5 | cm/cm/°C | TMA |
| Thermal Conductivity | 0.51 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.5E+12 | ohms | IEC 60093 |
| Volume Resistivity | 2.1E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 28 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm, Tested by SBHPP | V-0 | UL 94 | |
| 3.0 mm, Tested by SBHPP | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durez® 33897 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Geon™ Vinyl Flexible R293AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hyundai EP PA66 LD460C | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Petlon Prime A2-G25-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |
| Petrothene® NA442051 | LyondellBasell Industries | LDPE | Petrothene® |