Generic PMP Copolymer
| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vw7zN3_Generic-PMP-Copolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PMP Copolymer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.833 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 18 to 26 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 1.5 to 2.1 | % | |
| Across Flow : 23°C | 1.1 to 1.7 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 42 to 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 785 to 1920 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 20.0 to 30.2 | MPa | |
| Break, 23°C | 10.0 to 25.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 11 to 60 | % | ASTM D638 |
| Flexural Modulus (23°C) | 630 to 1770 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 21.0 to 51.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 19 to 28 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 8.0 to 130 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 75.0 to 128 | °C | ASTM D648 |
| Vicat Softening Temperature | 151 to 177 | °C | ASTM D1525 |
| Melting Temperature | 222 to 237 | °C | |
| CLTE - Flow | 1.2E-4 to 3.8E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C) | 63 to 66 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 2.10 to 2.12 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 to 1.463 | ASTM D542 | |
| Transmittance | 93.0 to 94.0 | % | ASTM D1003 |
| Haze | 0.70 to 2.1 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 136F4Q32 | SAX Polymers | Nylon 6 | SAXAMID™ |
| INSTRUC POMCGF20 | Infinity LTL Engineered Compounds | Acetal (POM) Copolymer | INSTRUC |
| LOXIM 220 01 HB | LOXIM Industries Private Limited | PBT | LOXIM |
| InnoPlus HD2218J | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| OnForce™ LFT AM-60LGF/001 BLACK | PolyOne Corporation | PPA | OnForce™ LFT |