OmniCarb™ PC/PBT 1020 FR0
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniCarb™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vvRgUm_OmniCarb-PC-PBT-1020-FR0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame Resistant, PC/PBT |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 61.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 98.9 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | V-0 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 249 to 277 | °C | |
| Front Temperature | 249 to 277 | °C | |
| Nozzle Temperature | 249 to 277 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Restren ABS 766/V0 | Polimarky Spolka Jawna | ABS | Restren |
| 3M™ Dyneon™ Fluoroelastomer FPO 3630 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Elastron® G P.G300.A36.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina BLACK PVC COMPOUND 70900-48/1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Capilene® QC 56 E | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |