VITAMIDE® AP36NT6567
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vvKl9X_VITAMIDE-AP36NT6567.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AP36NT6567 is a Polyamide 66 (Nylon 66) product filled with 20% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | |||
| 24 hr | 0.80 | % | ASTM D570 |
| 23°C, 24 hr | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 150 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6500 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 220 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 255 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 1218, ASTM D2117 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257, IEC 60093 |
| Dielectric Strength | 21 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 450 | V | IEC 60112 |
| -- | 450 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 27 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® S4665 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Thermylene® P7-40FG-1804 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Avalon 30 | Greene, Tweed & Co. | PTFE | Avalon |
| Hostaform® CF802 10/9022 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Sylvin 9928-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |