Ultradur® B 4406 G6 Q113
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vuKUGI_Ultradur-B-4406-G6-Q113.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection molding grade with 30% glass fibers for parts requiring enhanced fire resistance (eg relay housings, plug-in connector, switch and lamp parts) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 19.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.94 | % | |
| Flow | 0.28 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number 1 | 108 | cm³/g | ISO 307 |
| Mold Shrinkage 2 | |||
| free, longitudinal | 0.30 | % | |
| free, transverse | 1.1 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability by Electrical Sources of Ignition - Method BH (4.00 mm) | BH2 | IEC 60707 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | PBT, MFGHLNR, 11-120, GF30 | ISO 7792 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | < 250 | mm/sec |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2 |
| Flexural Stress | 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/A |
| Melting Temperature | 223 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 2.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.4E-3 | ||
| 1 MHz | 0.016 | ||
| Comparative Tracking Index (Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 2 . | plate with film gate 150*150*3 mm³ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E185 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Shandong PP PG8101 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| ULTEM™ HU2200 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| DeWAL DW 402P | DeWAL Industries | UHMWPE | DeWAL |
| Enable™ 27-05HH | ExxonMobil Chemical | mPE | Enable™ |