| 4TECH 9S22110 is a Standard Flow 10% Glass Fibre Reinforced PPO |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Moisture Content | < 2000 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4750 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Screw Speed | 250 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-1805IMLM | QTR, Inc. | PC+Polyester | QR Resin |
| WanBlend® WHT-THF9485T2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Daelim Po1y® PP-101 | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| Sylvin 8887-95 Brown 7395 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ PX1390 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |