Evoprene™ COGEE 681
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | AlphaGary |
| Trademark: | Evoprene™ COGEE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vtk53i_Evoprene-COGEE-681.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The Evoprene COGEE range was specially developed to provide materials which will comould or coextrude to engineering thermoplastics (ETPs). This enables, for example, polyamide (nylon) handles or ABS housings to be given a solt touch feel whilst polycarbonate lenses can have gaskets moulded on to provide a weathertight product. The Evoprene COGEE grades are modified Kraton G based compounds. Many of the characteristics exhibited by the Evoprene G and Evoprene Super G ranges are shown by Evoprene COGEE compounds. However, they do have to be processed quite differently to obtain optimum bond strengths and performance characteristics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 40 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% Strain | 1.40 | MPa | |
| 300% Strain | 2.80 | MPa | |
| Tensile Stress (Yield) | 2.70 | MPa | ISO 37 |
| Tensile Elongation (Break) | 460 | % | ISO 37 |
| Tear Strength 1 | 21 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 28 | % | |
| 70°C, 22 hr | 56 | % | |
| 100°C, 22 hr | 43 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -30 to 100 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bond Strength | 0.710 | MPa | Internal Method |
| M-S Flow | 2.75 | MPa | Internal Method |
| Ozone Resistance 2(35°C) | No Cracks | ISO 1431-1 | |
| UV Rating 3(40°C) | No Visible Cracks or Crazing |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Rate | Fast | ||
| Vent Depth | 0.020 to 0.050 | mm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| 2 . | 100 pphm/200 hrs/20% Strain |
| 3 . | 350 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| K-Prene XL-A40 | Technovinyl Polymers India Ltd. | PP+EPDM | K-Prene |
| LNP™ THERMOCOMP™ JF004P compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |
| Sylvin 83018-80UV White 1578 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ESTOPLAST ZK 8508BB01 | Ester Industries Ltd. | PC+ABS | ESTOPLAST ZK |
| Sylvin 8784-77 Black 280 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |