VITAMIDE® AR16WT6307
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vtFIXE_VITAMIDE-AR16WT6307.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AR16WT6307 is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 160 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8300 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 250 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 75 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 255 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 1218, ASTM D2117 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257, IEC 60093 |
| Dielectric Strength | 24 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 450 | V | IEC 60112 |
| -- | 450 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 10 | RTP Company | Nylon 66 | RTP |
| PrimoTek KM6130 | KMI Group Inc. | PBT | PrimoTek |
| Spartech Polycom EP6140 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| CERTENE鈩?HI-954 | Muehlstein | HDPE | CERTENE™ |
| Geon™ Vinyl Rigid Extrusion L1101 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |