NuSil MED-4780
| Category: | Rubber , Rubber |
| Manufacturer: | NuSil Technology |
| Trademark: | NuSil |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vt2hsZ_NuSil-MED-4780.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NuSil Technology's unrestricted materials may be considered for long-term implant applications (greater than 29 days). High consistency rubber, or HCR, consists of high molecular weight polymer combined with silica to produce a material that can be molded, extruded, or calendared into a useful end product. An HCR has the consistency of clay and is primarily formulated in a one or two part system (peroxide and platinum catalysts, respectively). Most platinum cure high consistency rubbers are two component systems with an easy-to-work-with 1:1 mix ratio. Comments: HIGH TEAR |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (200% Strain) | 3.28 | MPa |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 1.0 | ||
| Component B | Mixing ratio by weight: 1.0 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure System | Platinum | ||
| Plasticity: 145 mils |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.21 | g/cm³ | |
| Curing Time (116°C) | 0.17 | hr | |
| Pot Life (25°C) | 270 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 80 | ||
| Tensile Strength | 7.58 | MPa | |
| Tensile Elongation at Break | 700 | % | |
| Tear Strength | 37.7 | kN/m |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVADURAN® 5010GT15X | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| FLEXOMER™ DFDA-1137 NT 7 | The Dow Chemical Company | VLDPE | FLEXOMER™ |
| Hostacom TRC 1193N | LyondellBasell Industries | TPO (POE) | Hostacom |
| LNP™ THERMOCOMP™ QC008 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| Lucent PP PPH-110 | Lucent Polymers, Inc. | PP Homopolymer | Lucent PP |