Sindustris ABS LAF471S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vswYFn_Sindustris-ABS-LAF471S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TBBA-free Flame Retardant |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2160 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 42.2 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20 mm | 5.0 | % | |
| Break, 3.20 mm | 20 | % | |
| Flexural Modulus 4(6.40 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 5(6.40 mm) | 66.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 78 | J/m | |
| -30°C, 6.40 mm | 69 | J/m | |
| 23°C, 3.20 mm | 250 | J/m | |
| 23°C, 6.40 mm | 180 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 95.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 6 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | V-0 5VA | ||
| 3.00 mm | V-0 5VA |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Melt Temperature | 200 to 230 | °C | |
| Die Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP MDPE 003937 | Amco Polymers | MDPE | PRIMATOP |
| Complet® LGF50-PPA | PlastiComp, Inc. | PPA | Complet® |
| Expandable PS F32B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Hostacom TRC 787N | LyondellBasell Industries | TPO (POE) | Hostacom |
| Sylvin 4200-80UV Grey 9539 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |