NYCOA Polyamide 5013 HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vshSS0_NYCOA-Polyamide-5013-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 5013 HS is a 13% glass fiber reinforced, heat stabilized Nylon 66 resin used for injection molding. NYCOA 5013 HS offers better mechanical and thermal properties than most conventional Nylon 66. This grade is available in light stable, flame retardant and custom color formats. Typical applications include electrical connectors, circuit breaker parts and automotive under the hood applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.70 | % | ASTM D955 |
| Transverse flow | 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5400 | MPa | ASTM D638 |
| Tensile Strength 2 | 112 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 4790 | MPa | ASTM D790 |
| Flexural Strength 5 | 158 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 249 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 232 | °C | ASTM D648 |
| Melting Temperature | 258 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HHM 5502LD | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Triapol® Blends C3 K28 PRTA010 BS302 | Petropol Industry and Trade of Polymers LTDA | PC+ABS | Triapol® Blends |
| EPO-TEK® CF6-2 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| InnoPlus LD2420K | PTT Global Chemical Public Company Limited | LDPE | InnoPlus |
| LUBAN™ 1102 K | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |