Politer 30 GB
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Poliblend S.p.a. |
| Trademark: | Politer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vrL3EF_Politer-30-GB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Politer 30 GB is a Polybutylene Terephthalate (PBT) material filled with 30% glass bead. It is available in Africa & Middle East, Asia Pacific, Europe, or Latin America. Primary attribute of Politer 30 GB: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.4 to 1.8 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 75.0 | MPa | |
| Break | 75.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.5 | % | |
| Break | 3.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 3.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 195 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 130 | °C | |
| Vicat Softening Temperature | 195 | °C | ISO 306/A120 |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 225 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | > 3.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Without Load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® LL 24050 | Plastic Solutions, Inc. | LLDPE | PrimaFlex® |
| Shuang-Bang C-0155H | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| Unipren® Elastomers A3 NTLA010 65A UP323 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| INEOS PP H03W-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| Karina WHITE COLOR CONCENTRATE -E 1-/105-FC-LMPA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |