MAJORIS FFR067 - 5168
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vqBaYH_MAJORIS-FFR067---5168.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FFR067 - 5168 is part of a new material family with low halogen no blooming flame retardant, high impact strength, high gloss and antistatic as well as an excellent UV-resistance and very low war page behaviour. Intended for injection moulding. The product is available in natural (FFR067) but other colours can be provided on request. APPLICATIONS FFR067 - 5168 is recommended for indoor or outdoor electrical and lighting applications like plugs, sockets, connectors, capacitor housings, small junction boxes or lamp covers; where chemical resistance, impact and flammability behaviours are required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.965 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow | 1.2 | % | |
| Flow : 2.00 mm | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1250 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 22.0 | MPa | ISO 527-2/50 |
| Break | 10.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 7.0 | % | ISO 527-2/50 |
| Break | 90 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 85 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 88.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A |
| -- | 75.0 | °C | ISO 306/B |
| Ball Pressure Test (125°C) | Pass | IEC 60335-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 7.8E+15 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 41 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.25 | ||
| 1 kHz | 2.25 | ||
| 100 kHz | 2.24 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.5E-3 | ||
| 1 kHz | 1.5E-3 | ||
| 100 kHz | 2.0E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | > 600 | V | |
| Solution B | > 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, All) | V-2 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.500 mm | 850 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature (1.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solarkote® P-601 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Solarkote® |
| Jamplast Ex-03 ABS | Jamplast, Inc. | ABS | Jamplast |
| Plexiglas® 8H | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| TECHNYL® A 217 BLACK 61 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| THERMOLAST® K TF7ADN (Series: FC/AD1/PS) | KRAIBURG TPE | TPE | THERMOLAST® K |