Eraclene® SB 60
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vpwg6a_Eraclene-SB-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene SB 60 is a high density polyethylene resin (HDPE), with antioxidants, suitable for sheets application. The resin is appreciated for its white colour, excellent extrudability, good rigidity, very low water vapour permeability, good sealability and high resistance to low temperature. Main Application Eraclene SB 60 is recommended for the production of extruded sheets to be used as semi finished items for thermoforming and protection profiles for metallic parts. Thanks to high noise absorption, the sheets produced by Eraclene SB 60 can be used as acoustic insulator for barrier construction. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.40 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 22.0 | MPa | |
| Break, Compression Molded | 31.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | > 800 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(Compression Molded) | 260 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ISO 306/A |
| Melting Temperature | 132 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D TFE 15 | RTP Company | Nylon 612 | RTP |
| SAXALEN™ PPH327G28 | SAX Polymers | PP Homopolymer | SAXALEN™ |
| Teflon® PTFE DISP 30 | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| NuSil MED-5440 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| ISPLEN® PG 340 AT | REPSOL | PP Homopolymer | ISPLEN® |