Generic PFA
| Category: | PFA , Perfluoroalkoxy |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vp2ttn_Generic-PFA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PFA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 2.14 - 2.15 | g/cm³ | ASTM D792 |
| 23°C | 2.13 - 2.15 | g/cm³ | ISO 1183 |
| Apparent Density | 0.55 - 1.20 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | |||
| 372°C/5.0 kg | 1.7 - 26 | g/10 min | ASTM D1238 |
| 372°C/5.0 kg | 1.7 - 16 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 55 - 60 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture, 23°C | 20.7 - 26.1 | MPa | ASTM D638 |
| Fracture, 23°C | 26.0 - 35.0 | MPa | ISO 527-2 |
| 23°C | 25.0 - 29.0 | MPa | ASTM D638 |
| 23°C | 25.0 - 28.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 300 | % | ASTM D638 |
| Fracture, 23°C | 290 - 420 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 543 - 690 | MPa | ASTM D790 |
| 23°C | 550 - 627 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 305 - 311 | °C | |
| CLTE - Flow | 1.2E-4 - 1.6E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat (23°C) | 1.00 - 1050 | J/kg/°C | ASTM C351 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 7.5E+16 - 1.0E+18 | ohms·cm | ASTM D257 |
| 23°C | 9.8E+17 - 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 37 - 81 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 2.00 - 2.10 | ASTM D150 | |
| Dissipation Factor (23°C) | 2.0E-4 - 5.0E-4 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 399 - 400 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PFAThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB1000-10 | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| Ultralloy™ 203 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| CONAP® CE-1171 | Cytec Industries Inc. | Acrylic, Unspecified | CONAP® |
| ELASTOSIL® R plus 4000/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| PENTAMID A L10 H natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |