EMAC® SP2258
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | EMAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | voc9b2_EMAC-SP2258.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Westlake EMAC® SP2258 is a 17% EMA copolymer containing slip and antiblock. This resin is designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat seal temperatures are required. SP2258 provides excellent adhesion to polyolefins, polyesters, and other polymers while providing outstanding low temperature performance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.943 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
| Methyl Acrylate Content | 17.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 37 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 12.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 730 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Blown Film | 56.0 | MPa | |
| 1% Secant, TD : 38 µm, Blown Film | 59.0 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 21.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 16.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 330 | % | |
| TD : Break, 38 µm, Blown Film | 660 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 300 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Blown Film | 53 | g | |
| TD : 38 µm, Blown Film | 340 | g | |
| Seal Initiation Temperature | 70.0 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -73.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 56.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 82.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm, Blown Film) | 15 | ASTM D2457 | |
| Haze (38.1 µm, Blown Film) | 53 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Type IV, 500 mm/min |
| 2 . | Type IV, 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 4 Series 498A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 4 Series |
| Vipel® F701-FBG-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| NYLOY® PG-2040N | Nytex Composites Co., Ltd. | PP, Unspecified | NYLOY® |
| apilon 52® ETC 42 | API SpA | TPU-Polyether | apilon 52® |
| Sylvin 9604-80 Clear 8478 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |