NANCAR® 1204D
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vo870z_NANCAR-1204D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 1204D is a fluxed blend of 100 parts NBR, 60 parts PVC and 120 parts DEHP. This polymer has sufficient stabilizer for normal aging conditions and can be processed with normal mixing procedures. It has good processability for extrusion, providing smooth surfaces on the resultant product. NANCAR® 1204D is excellent in low hardness application and resistance to abrasion, ozone, oil and fuel. It is suggested to be use in low hardness printing plates and rolls. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 100°C) | 29 | MU | ASTM D1646 |
| Acrylonitrile Content - Bound | 33.0 | % | Internal Method |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Compression Set - 70 hrs (100°C) | 70 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.30 | % | ASTM D5688 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ozone Resistance - 50 pphm X 40°C X 20% 1 | no crack |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 68 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Yield) | 14.3 | MPa | |
| Tensile Elongation (Break) | 460 | % |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 70 hr) | -4.0 | % | |
| Change in Ultimate Elongation in Air (100°C, 70 hr) | -24 | % | |
| Change in Durometer Hardness in Air (100°C, 70 hr) | 2.0 | ||
| Change in Tensile Strength | |||
| 100°C, 70 hr, in ASTM #1 Oil | 1.0 | % | |
| 100°C, 70 hr, in IRM 903 Oil | -5.0 | % | |
| Change in Ultimate Elongation | |||
| 100°C, 70 hr, in ASTM #1 Oil | -54 | % | |
| 100°C, 70 hr, in IRM 903 Oil | -42 | % | |
| Change in Durometer Hardness | |||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | 29 | ||
| Shore A, 100°C, 70 hr, in IRM 903 Oil | 24 | ||
| Change in Volume | |||
| 100°C, 70 hr, in ASTM Oil #1 | -33 | % | |
| 100°C, 70 hr, in IRM 903 Oil | -23 | % |
| Note Message | |
|---|---|
| 1 . | at 24 hrs, 48 hrs, 72 hrs, 96 hrs, 168 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® FP10KSC | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Monprene® SP-13064 | Teknor Apex Company | TPE | Monprene® |
| Cellophane™ 335WSZB | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Generic PP Impact Copolymer - Mineral | Generic | PP Impact Copolymer | Generic |
| Laprene® 83FM00A30 | SO.F.TER. SPA | SEBS | Laprene® |