Zytel® FR70G25GWNH WT409
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vnDie4_ZytelFR70G25GWNHWT409.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% Glass Reinforced, Flame Retardant, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.80 | -- | % | ISO 294-4 |
| Flow | 0.20 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 125 | 73.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 3.7 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 4.5 | 5.2 | kJ/m² | ISO 179/1eA |
| 23°C | 3.4 | 4.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 27 | 34 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 3.5 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 237 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 261 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 290 | °C | |
| Mold Temperature, Optimum | 100 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Ejection Temperature | 210 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HKR102 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| DOW™ HDPE DMDA-8904 NT 7 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Network Polymers PC 1900 | Network Polymers, Inc. | PC | Network Polymers PC |
| BCC Resins DP-11-83 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| Rotec® ABS 1001 GK20 | ROMIRA GmbH | ABS | Rotec® ABS |