DOW™ LLDPE DFDC-7087 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vmuRpr_DOW-LLDPE-DFDC-7087-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dow Linear Low Density Polyethylene DFDC-7087 NT 7 is a Linear Low Density Polyethylene Resin material,. This product is available in North America and is processed by blowing film. The main characteristics of Dow linear low density polyethylene DFDC-7087 NT 7 are:
The typical application field of Dow linear low density polyethylene DFDC-7087 NT 7 is: food contact application |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | Internal method |
| Film Puncture Energy | 1.47 | J | Internal method |
| Film Puncture Force | 26.7 | N | Internal method |
| Film Puncture Resistance | 8.11 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 109 | J/cm³ | ASTM D882 |
| TD | 107 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 216 | MPa | ASTM D882 |
| 2% secant, MD | 190 | MPa | ASTM D882 |
| 1% secant, TD | 246 | MPa | ASTM D882 |
| 2% secant, TD | 206 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.7 | MPa | ASTM D882 |
| TD : Yield | 11.6 | MPa | ASTM D882 |
| MD : Fracture | 40.5 | MPa | ASTM D882 |
| TD : Fracture | 29.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 580 | % | ASTM D882 |
| TD : Fracture | 680 | % | ASTM D882 |
| Dart Drop Impact | 95 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 160 | g | ASTM D1922 |
| TD | 400 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 17 | ASTM D2457 | |
| Haze | 38 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5in.; 30:1ratio L/D Screw Type: DSB II Die Gap: 70 mil (1.8 mm) Melt Temperature: 417°F Output: 12 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 39 rpm Frost Line Height: 52 in |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4190 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RENOL® Engineering Resin Color Masterbatch | Clariant Corporation | TP, Unspecified | RENOL® |
| VENYL UN000 - 8229 | AD majoris | Nylon 66 | VENYL |
| Lupoy® GP5008BFH | LG Chem Ltd. | PC+ABS | Lupoy® |
| ESTOPLAST XU 225GY78 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |