Order Products : sales@su-jiao.com

KPOL-HDPE HD K-5.5/954

Category:	HDPE, HMW , High Density (HMW) Polyethylene
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vloXiV_KPOL-HDPE-HD-K-5-5-954.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High Density Polyethylene Extra high molecular weight, hexene copolymer Extrusion-Blow Molding

Characteristics

The KPOL HD K5.5/954, is a high molecular weight high-density polyethylene, copolymer. Suitable for large parts blow molded an L-ring drum. Exhibit an good impact resistance and excellent stress cracking resistance (ESCR).

Applications

L-ring drum and general large parts blow molded, Industrial Tanks and 55-gallon drums.

The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Additive	Antioxidant
Features	Antioxidant Copolymer Food Contact Acceptable Good Impact Resistance High Density High ESCR (Stress Crack Resist.) High Molecular Weight
Uses	Drums Industrial Tanks Tanks
Agency Ratings	FDA 21 CFR 177.1520(c)
Processing Method	Blow Molding Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.954	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/21.6 kg)	5.5	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
50°C, 1.91 mm, 10% Igepal CO-630	500	hr	ASTM D1693B
50°C, 3.18 mm, 100% Igepal CO-630	> 1000	hr	ASTM D1693A

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	62		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	32.0	MPa	ASTM D638
Tensile Elongation (Break)	800	%	ASTM D638
Flexural Modulus - Tangent	1.32	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength	450	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -75.0	°C	ASTM D746
Vicat Softening Temperature	127	°C	ASTM D1525
Melting Temperature	140	°C	DSC
Heat Deflection Temperature	74	°C	ASTM D648

Resin Grade	Manufacturer	Category	Trademark
VITAMIDE® AR3XBK8510	Jackdaw Polymers	Nylon 66	VITAMIDE®
Ultradur® B 4040 G6 High Speed	BASF Corporation	PBT+PET	Ultradur®
AKROMID® B3 GM 15/15 black (1830)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
Clariant Nylon 6/6 PA-131G13	Clariant Corporation	Nylon 66	Clariant Nylon 6/6
Flontech® FT-GL15-M3-1	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®