EMOPLEN® AT 1002 RT2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | EMAS Plastik San.Tic.AS. |
| Trademark: | EMOPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | viwR35_EMOPLEN-AT-1002-RT2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene %20 talcum filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 to 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 to 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 to 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 to 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 to 3500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 to 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 6.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | > 2.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 160 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9515H | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| NEXUS Reprocessed HDPE 8/954 RBK | Nexus Resin Group, LLC. | HDPE | NEXUS Reprocessed |
| AKROLOY® PA GF 50 grey (3807) | AKRO-PLASTIC GmbH | Nylon 66+Nylon 6I/6T | AKROLOY® |
| TOTAL Polyethylene Lumicene® M 3583 UV (US) | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |
| LNP™ LUBRICOMP™ DBL32 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |