LNP™ STAT-KON™ KEL22A compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vitoKY_LNP-STAT-KON-KEL22A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP KEL22A is a compound based on Acetal Homopolymer resin containing Carbon Fiber, PTFE. Added features include: Electrically Conductive, Internally Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.33 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 56.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6100 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 89.0 | MPa | |
| -- 4 | 82.0 | MPa | |
| Flexural Strain at Break 5 | 7.9 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8(1.8 MPa, Unannealed, 64.0 mm Span) | 135 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.2E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 382 TFE 5 | RTP Company | PC | RTP |
| SABIC® HDPE A4046 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| TOTAL Polyethylene HDPE SB 1359 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Adsyl 5 C 30 F | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| GAPEX® HPP30GR29BK | Ferro Corporation | PP Homopolymer | GAPEX® |