PermaStat® 100 HI
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | PermaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vhG1O4_PermaStat-100-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Impact - ESD Protection - Permanently Anti-static |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 2.0 | % | ASTM D955 |
| Moisture Content | 0.10 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1030 | MPa | ASTM D638 |
| Tensile Strength | 18.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 896 | MPa | ASTM D790 |
| Flexural Strength | 25.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 800 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+10 - 9.9E+11 | ohms | ASTM D257 |
| -- | 1.0E+9 - 9.9E+10 | ohms | ESD STM11.11 |
| Volume Resistivity | 1.0E+9 - 9.9E+10 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 171 - 204 | °C | |
| Mold Temperature | 32.2 - 65.6 | °C | |
| Injection Pressure | 48.3 - 75.8 | MPa |
| Injection instructions |
|---|
| Do not exceed 520 °F (270 °C) melt temperature. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Softflex® 0470 | Network Polymers, Inc. | TPE | Softflex® |
| Vi-Chem PVC V221-80I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| YUNGSOX® PP 1250D | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| Laticonther 57 CPG/550 | LATI S.p.A. | PPA | Laticonther |
| Karina WHITE PVC COMPOUND -E 832-10/ 84-Y-ERM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |