Promyde® B30 P2 M30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vh9R8D_Promyde-B30-P2-M30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde® B30 P2 M30 is a Polyamide 6 injection moulding grade with 30% mineral filler and heat stabilised. CHARACTERISTICS Promyde B30 P2 M30 is distinguished by high mechanical strength, hardness, rigidity and thermo stability. Parts made from Promyde B30 P2 M30 have particularly high dimensional stability. APPLICATIONS Promyde B30 P2 M30 is used in a wide range of applications where a combination of mechanical properties and dimensional stability is needed. Mineral filler reinforced grades are suitable for housings, supports, industrial articles and electrical insulating parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.7 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5200 | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 80.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 3.0 | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 3900 | 2000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 94.0 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 5.3 | 25 | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 3 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | 6.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back Pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravaflex EPM P | Ravago Group | EPM | Ravaflex |
| RTP EMI 1562 | RTP Company | TPE | RTP |
| CP PRYME® Nylon 6 N100LZ NAT | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| DOMAMID® A1-008-V30-H2-DB | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Sylvin 6920X08 Grey 9610 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |