NYCOA Polyamide 2301
| Category: | Nylon+TPE , Polyamide + TPE |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vgeTC5_NYCOA-Polyamide-2301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2301 is a highly flexible Nylon copolymer TPE suitable for extrusion processing and injection molding. NYCOA 2301 processes easily at low injection pressure compared to other impact modified nylons. It can be molded and extruded on standard equipment. NYCOA 2301 is recommended for applications that require premium toughness such as hoses, connectors, tool housing, appliance parts, and hardware items. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | ASTM D955 |
| Transverse flow | 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 52.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 3 | 896 | MPa | ASTM D790 |
| Flexural Strength 4 | 35.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 212 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 232 - 249 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 300 90A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Sumitomo Phenolic FM 1132P | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| TRIREX® Compound 3025GRU20 | Samyang Corporation | PC | TRIREX® Compound |
| LNP™ STAT-KON™ KEL32 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ STAT-KON™ |
| Durethan® BKV 25 FN27 000000 | LANXESS GmbH | Nylon 6 | Durethan® |