BESTPOLUX PCX-01
| Category: | PC , Polycarbonate |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOLUX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vgKZ8g_BESTPOLUX-PCX-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC natural lubrified with V-0 quality is characterized for good flame retardant quality and injection behaviour. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.24 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 66.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+15 | ohms | IEC 60093 |
| Comparative Tracking Index | 225 | kV/mm | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Resistance | Yes, | ||
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Humidity Pellets, ISO 1110: 0.2%Flammability Speed, FMV 302:<100 mm/min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titacon® GB910L | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Europrene Latice® 406 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Iupilon® EFR3000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Karina NATURAL PVC COMPOUND 890-25/ 1-CR-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1105-0904/GN2 | LEHVOSS Group | PEEK | LUVOCOM® |