Nycal™ 2210
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Nycal™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vfSyHc_Nycal-2210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nycal™2210 is a polyamide material,. This product is available in North America and is processed by extrusion or injection molding. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 67.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 100 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 71.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 62.8 | °C | ASTM D648 |
| Melting Temperature | 73.9 | °C | DSC |
| Additional Information |
|---|
| Tensile Elongation, ASTM D638: >100% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 - 0.689 | MPa | |
| Screw Speed | 25 - 75 | rpm | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMORUN® QT80MA | Mitsubishi Chemical Corporation | TPO (POE) | THERMORUN® |
| Fiberfil® M-1812 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| KOCETAL® K700LO | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Karina WHITE PVC COMPOUND 800D10/7-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pibiter® N200 NAT001 | SO.F.TER. SPA | PBT | Pibiter® |