VTEC™ GF63

Category:	PI, TS , Thermoset Polyimide
Manufacturer:	RBI, Inc.
Trademark:	VTEC™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vf6Dqg_VTEC-GF63.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High temperature resistance

Strength at elevated temperature

Superior mechanical properties

High compressive strength and creep resistance

Excellent chemical resistance

Superior resistance to plasma etching

Outstanding electrical properties

Wear resistance, low friction, self-lubricating

Non-abrasive to mating parts

Extremely low moisture absorption

Radiation resistant

Compliant without deforming under load and temperature

Very low outgassing

Zero metal and mineral extractables

Extremely dimensionally stable

Equal CTE in X, Y and Z directions

General Information
Features	Good Chemical Resistance Good Compressive Strength Good Creep Resistance Good Dimensional Stability Good Electrical Properties Good Wear Resistance High Heat Resistance High Temperature Strength Low Extractables Low Friction Low Moisture Absorption Low to No Outgassing Radiation (Gamma) Resistant Self Lubricating
Forms	Customizable Forms Rod Sheet Tubing

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.87	g/cm³	ASTM D792
Water Absorption (Saturation, 24°C)	< 0.10	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Barcol Hardness	75		ASTM D2583

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
24°C	75.8	MPa
204°C	75.8	MPa
246°C	82.7	MPa
Flexural Modulus			ASTM D790
24°C	15900	MPa
204°C	14500	MPa
246°C	15200	MPa
Flexural Strength			ASTM D790
24°C	207	MPa
204°C	214	MPa
246°C	221	MPa
Compressive Strength - Open-Hole (246°C) ¹	Passed		ASTM D648

Flammability	Nominal Value
Flammability
-- ²	Non-burning, No drip, No glowing combustion
843°C	Non-burning, No drip, No glowing combustion

Additional Information	Nominal Value	Unit
Dimensional Stability, Shrinkage - 24 hrs (246°C)	0.0	%
Thermal Gravimetric Analysis (500°C)	No recordable weight loss
Thermal-oxidative Deterioration (182°C) ³	0.20	%

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (24°C)	800	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	270	°C
CLTE - Flow (75°C)	1.4E-5	cm/cm/°C	ASTM D696

Note Message
1 .	Hot, Wet
2 .	1000 BTU cu. ft
3 .	100 hrs, 60 psi loss

Resin Grade	Manufacturer	Category	Trademark
Quadrant EPP Armor-X™ Non-Marring	Quadrant Engineering Plastic Products	TP, Unspecified	Quadrant EPP
UNISOFT TPE™ ST-78A-NT-1-01	UNITED SOFT PLASTICS, Inc.	SEBS	UNISOFT TPE™
INEOS PP H03W-01	INEOS Olefins & Polymers USA	PP Homopolymer	INEOS PP
Adstif HA600U	LyondellBasell Industries	PP Homopolymer	Adstif
Novalloy-A A2606	PlastxWorld Inc.	ABS+Nylon	Novalloy-A