Plexiglas® MI7C-56503RB
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | veu8tb_Plexiglas-MI7C-56503RB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plexiglas® MI7C-56503RB is an impact modified thermoplastic acrylic resin formulated for injection molding. It is a jet black, high gloss, opaque resin that has high heat resistance, high melt flow and provides 7 times the impact resistance of standard acrylics while maintaining excellent optical properties. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Moldflow simulation data is available. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2410 | MPa | ASTM D638 |
| Tensile Strength (Break) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 100 | °C | |
| 1.8 MPa, Annealed | 95.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ASTM D1525 2 |
| -- | 96.1 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0241V3 | ASTM D788 |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 40YM240 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| Vi-Chem PVC V141-60 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Nucrel® 0903 | DuPont Packaging & Industrial Polymers | EMAA | Nucrel® |
| Geon™ Vinyl Rigid Extrusion 8700X | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Tribocomp® PA66 LGF30 PTFE18 N6 | Solvay Specialty Polymers | Nylon 66 | Tribocomp® |