Nymax™ GMF 604 40 UV Black 115 1 X 1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vehXlk_Nymax-GMF-604-40-UV-Black-115-1-X-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nymaxm®GMF600 series polymer products are a combination of nylon 6 resin and glass fiber or mineral reinforcement, which can maintain a unique balance between physical properties and component properties. These materials are dedicated to processing in standard thermoplastic processing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 0.30 - 0.40 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 3.18 mm | 0.80 | % | ASTM D570 |
| 23°C, 24 hr | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 7580 | MPa | ASTM D638 |
| -- | 7800 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield 1 | 117 | MPa | ASTM D638 |
| Yield | 100 | MPa | ISO 527-2 |
| Fracture 2 | 103 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 3 | 2.0 - 3.0 | % | ASTM D638 |
| Fracture | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7240 | MPa | ASTM D790 |
| -- | 7500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 172 | MPa | ASTM D790 |
| -- | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 64 | J/m | ASTM D256A |
| -- | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 190 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Molded Test Bars: Dry as Molded |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 48.9 - 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sekisui PVC HA-15F | Sekisui (Hong Kong) Limited | PVC, Unspecified | Sekisui PVC |
| DURANEX® 700FP | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Keyflex® TO 1088AV | LG Chem Ltd. | TPC-ET | Keyflex® TO |
| Hylon® N2200TL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Sumiliteresin® PR-53769 I | SBHPP | Phenolic | Sumiliteresin® |