LNP™ VERTON™ RV0079 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | veFkYd_LNP-VERTON-RV0079-compound-42262.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* RV0079 is a compound based on Nylon 66 resin containing Flame Retardant, Long Glass Fiber, Long Glass. Added features of this material include: Easy Molding. Also known as: LNP* VERTON* Compound RF-7007 FR Product reorder name: RV0079 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 213 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2 |
| Flexural Modulus | 13300 | MPa | ISO 178 |
| Flexural Stress | 298 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 33 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 58 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 262 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 259 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.70 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® K306 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| ALTECH® PA66 A 3040/100 GB40 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Garaflex™ O 9940 DWN-R NATURAL | AlphaGary | TPE | Garaflex™ O |
| PLANAC BT-2230-60 | TOYOBO America, Inc. | PBT | PLANAC |
| Sylvin 5132-86 Clear Green 3166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |