Maxxam™ FR C5 T-GF/10 XF V0 EP NC 70
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ FR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vdurGS_Maxxam-FR-C5-T-GF-10-XF-V0-EP-NC-70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-0, performance ratings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Across Flow : 23°C | 0.80 to 1.2 | % | |
| Flow : 23°C | 0.80 to 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm) | 2250 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C, 4.00 mm) | 25.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C, 4.00 mm) | 6.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/A120 |
| Melting Temperature | 160 to 165 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 to 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 to 3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 3.00 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | > 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | ±0.03 |
| 2 . | PolyOne Turkey method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RX® 1310 | Sumitomo Bakelite North America, Inc. | DAP | RX® |
| Spartech Polycom SC7-7210R | Spartech Polycom | PC | Spartech |
| DOW™ LLDPE DFDA-7047 NT 7 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| NORYL GTX™ GTX918W resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| Adiprene® LF 650D | Chemtura | PUR-Ether/TDI | Adiprene® |