Latilub 66-15ST G/30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vdQodC_Latilub-66-15ST-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Self-lubricating product based on Polyamide 66 (PA 66). Silicone / PTFE. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 to 1.2 | % | |
| Flow : 2.00 mm | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.28 | ||
| Wear Factor | 1.70E-7 | cm³·min/kg·m·h | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 3(23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 4(23°C) | 90 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 80x10x40 mm |
| 3 . | 80x10x40 mm |
| 4 . | 63.5x12.7x3.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil CV-2289-1 | NuSil Technology | Silicone | NuSil |
| Globalprene® 3501 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| HiCal™ LC | Heritage Plastics, Inc. | PP Impact Copolymer | HiCal™ |
| Pearlbond™ 523 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| PSM® HL-103 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |