DOW™ HDPE DMDA-8965 NT 7

Category:	HDPE , High Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vcG32W_DOW-HDPE-DMDA-8965-NT-7.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Injection molding

For injection molded thin-wall food containers

Excellent processability

Good impact strength and rigidity

Very narrow molecular weight distribution

Complies with U.S. FDA 21 CFR 177.1520 (c)3.1a

Complies with Canadian HPFB No Objection (With Limitations)

Complies with EU, No 10/2011

Complies with U.S. FDA DMF

Complies with U.S. FDA 21 CFR 177.1520(c)3.2a

Consult the regulations for complete details.

DOW DMDA-8965 NT 7 High Density Polyethylene (HDPE) Resin is produced via UNIPOL™ Process Technology from Dow and is intended for use in thinwall injection molding applications such as food containers. This resin has been designed to provide good toughness and excellent processability.

General Information
Agency Ratings	DMF not rated FDA 21 CFR 177.1520(c) 3.1a FDA 21 CFR 177.1520(c) 3.2a HPFB (Canada) No Objection 2 Europe No 10/2011
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.952	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	66	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	59		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	17.2	MPa	ASTM D638
Fracture	28.3	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	1.0	%	ASTM D638
Fracture	10	%	ASTM D638
Flexural Modulus - 2% Secant	1000	MPa	ASTM D790B

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength ¹	63.0	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	68.9	°C	ASTM D648
Brittleness Temperature	-75.0	°C	ASTM D746
Vicat Softening Temperature	122	°C	ASTM D1525
Melting Temperature (DSC)	128	°C	Internal method
Peak Crystallization Temperature (DSC)	116	°C	Internal method

Additional Information
根据 ASTM D 4976 进行基板模制和测试。

Note Message
1 .	Type s

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3617	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
TRILOY® CF210S	Samyang Corporation	PC+ABS	TRILOY®
Witcom PS 2006/086	Witcom Engineering Plastics B.V.	PS (GPPS)	Witcom PS
3M™ Dyneon™ PTFE Compound TF 6221	3M Advanced Materials Division	PTFE	3M™ Dyneon™ PTFE Compound
COPYLENE® CH034W	Phillips 66	PP Homopolymer	COPYLENE®