Iupilon® LGH2230M
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vc7uZx_Iupilon-LGH2230M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® LGH2230M is a Polycarbonate (PC) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® LGH2230M are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.1 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 4.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.25 to 0.45 | % | |
| Flow : 3.20 mm | 0.050 to 0.25 | % | |
| Water Absorption (Saturation, 23°C) | 0.090 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 111 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ISO 178 |
| Flexural Stress | 174 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 143 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AESN Noir T6L | Arkema | Nylon 12 | Rilsamid® |
| Durez® 33349 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Karina GREEN PVC COMPOUND 902-40/485-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OmniLon™ PA6/6 GR30 HSH BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| 3M™ Dyneon™ Fluoroelastomer FT 2481 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |