DOWLEX™ 2045
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vbpygY_DOWLEX-2045.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance | Internal method | ||
| 20 µm | 22.2 | J/cm³ | Internal method |
| 51 µm | 19.4 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 20 µm | 319 | J/cm³ | ASTM D882 |
| MD : 51 µm | 346 | J/cm³ | ASTM D882 |
| TD : 20 µm | 356 | J/cm³ | ASTM D882 |
| TD : 51 µm | 351 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 20 µm | 210 | MPa | ASTM D882 |
| 2% secant, MD : 51 µm | 194 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 232 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 233 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 11.8 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 10.9 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 12.1 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.3 | MPa | ASTM D882 |
| MD : Break, 20 µm | 64.2 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 55.1 | MPa | ASTM D882 |
| TD : Break, 20 µm | 52.7 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 49.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 640 | % | ASTM D882 |
| MD : Fracture, 51 µm | 830 | % | ASTM D882 |
| TD : Break, 20 µm | 880 | % | ASTM D882 |
| TD : Fracture, 51 µm | 890 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709A | ||
| 20 µm | 150 | g | ASTM D1709A |
| 51 µm | 290 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 230 | g | ASTM D1922 |
| MD : 51 µm | 900 | g | ASTM D1922 |
| TD : 20 µm | 520 | g | ASTM D1922 |
| TD : 51 µm | 1200 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 108 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 20.3 µm | 63 | ASTM D2457 | |
| 45°, 50.8 µm | 60 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 20.3 µm | 9.0 | % | ASTM D1003 |
| 50.8 µm | 10 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：DSBII 模具间隙：70 密尔 (1.8 mm) 熔体温度： 450°F (232°C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：83 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULABLEND® (ABS/PA) M/MK | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |
| Unichem 1116G-015 | Colorite Polymers | PVC, Flexible | Unichem |
| BMC 604 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Geon™ Vinyl Flexible R5185A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Karina WHITE PVC COMPOUND -E 839-10/ 68-Y-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |