LEXAN™ 4501 resin
| Category: | PC , Polyphthalate Carbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vbmamh_LEXAN4501resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN 4501 is a copolymer of polyphtalate carbonate resin for applications requiring high heat resistance. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.70 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 7.0 | % | ISO 527-2/50 |
| Fracture | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 59 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 5 | ISO 180/1A | ||
| -30°C | 11 | kJ/m² | ISO 180/1A |
| 23°C | 50 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 160 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Thermal Conductivity | 0.21 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (1 MHz) | 3.00 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.024 | IEC 60250 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 125 - 135 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 310 - 330 | °C | |
| Front Temperature | 320 - 340 | °C | |
| Nozzle Temperature | 320 - 340 | °C | |
| Processing (Melt) Temp | 325 - 360 | °C | |
| Mold Temperature | 100 - 125 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 sp=62mm |
| 5 . | 80*10*3 |
| 6 . | 80*10*3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1500-40D UV NATURAL | RTP Company | TEEE | RTP |
| S&E PVC GPT-76-1 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Visico™ LE4427/Ambicat™ LE4476 | Borealis AG | XLPE | Visico™ |
| NOVADURAN® 5010N6-3X | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Delta ATL C9CL | Delta Polymers | Acetal (POM) Copolymer | Delta |