SABIC® HDPE F0863
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vaP3GP_SABIC-HDPE-F0863.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE F0863 resin is a homopolymer with a very high density manufactured by gas phase technology. The grade offers high stiffness, high temperature resistance, low water vapour transmission and a very low gel level. Because of the linear character it is advisable to use the material in combination with extrusion coating LDPE grades like SABIC® LDPE 2005EC in order to improve extrusion coating processability (motorload and Neck In). Application SABIC® HDPE F0863 is typically used for food packaging, release paper and photographic paper. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.964 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, Cast Film | 580 | MPa | |
| TD : 25 µm, Cast Film | 580 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Cast Film | 26.0 | MPa | |
| TD : Yield, 25 µm, Cast Film | 24.0 | MPa | |
| MD : Break, 25 µm, Cast Film | 22.0 | MPa | |
| TD : Break, 25 µm, Cast Film | 18.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Cast Film | 700 | % | |
| TD : Break, 25 µm, Cast Film | 800 | % | |
| Oxygen Permeability (23°C, 25 µm, Cast Film) | 0.100 | cm³/m²/24 hr | Internal Method |
| Water Vapor Transmission Rate (38°C, 100% RH, 25 µm, Cast Film) | 4.0 | g/m²/24 hr | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 130 | °C | ISO 306/A |
| Melting Temperature (DSC) | 134 | °C | DIN 53765 |
| Enthalpy Change | 224 | J/g | DIN 53765 |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Minimum Coating Weight 1 | 2.0 | g/m² | Internal Method |
| Neck-in 2 | 168.0 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Measured on pilot line at 400 m/min, 300°C, airgap 300 mm |
| 2 . | Measured on pilot line at 200 m/min, 300°C, 10 g/m², airgap 300 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP CPC04C | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PP |
| Toraycon® 5101G-30U | Toray Resin Company | PBT | Toraycon® |
| NEXT REGRIND PBT 420SEO-100RG | NEXT Specialty Resins, Inc. | PBT | NEXT REGRIND |
| ENFLEX V1070A BLK UV | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| LNP™ LUBRILOY™ RF206XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |