EVAL™ E105B
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | EVAL Europe nv |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vaGo6k_EVAL-E105B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EVAL™ E105B is an Ethylene Vinyl Alcohol (EVOH) product. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 5.7 | g/10 min | |
| 210°C/2.16 kg | 13 | g/10 min | |
| 230°C/2.16 kg | 25 | g/10 min | |
| Ethylene Content | 44.0 | mol% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 11 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability 1 | ISO 14663-2 | ||
| 20°C, 0% RH | 0.016 | cm³·mm/m²/atm/24 hr | |
| 20°C, 35% RH | 0.022 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 0.030 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.066 | cm³·mm/m²/atm/24 hr | |
| 20°C, 90% RH | 0.088 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 2 | 0.81 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -- | 2.0 | kJ/m² | |
| -40°C | 2.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 53.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 156 | °C | ISO 306 |
| Melting Temperature | 165 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 145 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Annex C |
| 2 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BIOPLAST® GF 106/02 | BIOTEC GmbH & Co. KG | TP, Unspecified | BIOPLAST® |
| Alathon® M5363 | LyondellBasell Industries | HDPE | Alathon® |
| ESPOLEX 903 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| Lucene™ LC165 | LG Chem Ltd. | TPO (POE) | Lucene™ |
| Luxus PP 16052 | Luxus Limited | PP, Unspecified | Luxus PP |