Infino HA-4350G
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vZvZUd_InfinoHA4350G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HA-4350G is a polyxylene amide (PPA) product, which contains glass fiber reinforcement. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. The main characteristics are: heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 17 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.32 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.46 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.46 | % | ISO 2577 |
| Traffic : 3.20mm | 0.32 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 124 | ASTM D785 | |
| R scale | 124 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6960 | MPa | ASTM D638 |
| -- | 7000 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 206 | MPa | ASTM D638 |
| Yield | 215 | MPa | ISO 527-2/5 |
| Fracture 3 | 206 | MPa | ASTM D638 |
| Fracture | 215 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 4.1 | % | ASTM D638 |
| Fracture | 4.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 10800 | MPa | ASTM D790 |
| -- 6 | 10500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 275 | MPa | ASTM D790 |
| -- 8 | 275 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 74 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 74 | J/m | ASTM D256 |
| 23°C 10 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 290 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 290 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vitaster® UR34BK6223 | Jackdaw Polymers | PBT | Vitaster® |
| Vi-Chem PVC VNC80E | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Halene P F103 | Haldia Petrochemicals Ltd. | PP Homopolymer | Halene P |
| Lupox® GP2306FC | LG Chem Ltd. | PBT | Lupox® |
| Magnobond 1065-7 | Magnolia Plastics, Inc. | Epoxy | Magnobond |