KumhoSunny PC/PBT HCB9320G
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vZmqac_KumhoSunny-PC-PBT-HCB9320G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HCB9320G is a 20% glass fiber reforced PC/PBT alloy resin, offering high heat resistance, high mechanical strength and excellent chemical resistance. HCB9320G is recommended for automobile laggage carrier, household appliance, electrician products, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.42 | g/cm³ | ASTM D792 |
| -- | 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/5.0 kg | 18 | g/10 min | ASTM D1238 |
| 250°C/5.0 kg | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 to 0.60 | % | ASTM D955 |
| -- | 0.40 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 100 | MPa | ASTM D638 |
| -- | 105 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 5200 | MPa | ASTM D790 |
| -- 1 | 5500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 140 | MPa | ASTM D790 |
| -- 2 | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 3.20 mm | 110 | J/m | ASTM D256 |
| 23°C | 11 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 70 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 3 | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 240 to 275 | °C | |
| Front Temperature | 240 to 275 | °C | |
| Nozzle Temperature | 245 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Smooth-On Super Instant® | Smooth-On, Inc | Epoxy | Smooth-On |
| THERMOLAST® K TP7HPG (Series: EX/UV) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Borealis PP HF136MO | Borealis AG | PP Homopolymer | Borealis PP |
| DynaPath™ C2010CF | Polymer Dynamix | PC | DynaPath™ |
| Hiprolon® 11 ESNNHL P20 | Arkema | Nylon 1012 | Hiprolon® |