Adsyl 5 C 37 F
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adsyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vZEQiu_Adsyl-5-C-37-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adsyl 5 C 37 F is an advanced polyolefin, specially designed for use as a sealing layer in co-extruded film applications. This grade features a very low seal initiation temperature. It contains slip and anti-block additives. For regulatory information please refer to Adsyl 5 C 37 F Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 21.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 1 | 648 | MPa | ASTM D790A |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3/25 | ||
| MD : 50 µm, Cast Film | 280 | MPa | |
| TD : 50 µm, Cast Film | 280 | MPa | |
| Tensile Stress | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 14.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 14.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 45.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 35.0 | MPa | |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 17 | % | |
| TD : Yield, 50 µm, Cast Film | 15 | % | |
| MD : Break, 50 µm, Cast Film | 900 | % | |
| TD : Break, 50 µm, Cast Film | 800 | % | |
| Seal Initiation Temperature | 105 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 62.8 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 62.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 107 | °C | ISO 306/A50 |
| Melting Temperature | 132 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 87 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ SC-300 | Idemitsu Kosan Co., Ltd. | PC+PET | TARFLON™ |
| NYCOA Polyamide 2063 | Nycoa (Nylon Corporation of America) | Nylon 66/6 | NYCOA Polyamide |
| ADENE NHFA | A.D. Compound spa | PP Homopolymer | ADENE |
| Karina COMP. PVC BRANCO -E 703D10/ 58-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PEARLSTICK® 45-40/27 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |