Andur 2-95AP/Curene® 280
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vZ8id1_Andur-2-95AP-Curene-280.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| All properties based on Andur® 2-95AP cured with Curene® 280 |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 18.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 520 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 6.92 | MPa | ASTM D412 |
| 300% strain | 9.83 | MPa | ASTM D412 |
| Tear Strength | |||
| -- 1 | 77.1 | kN/m | ASTM D624 |
| Cracking | 39 | kN/m | ASTM D470 |
| Compression Set | 36 | % | ASTM D395 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Post Cure Time (23°C) | 72 | hr |
| Additional Information |
|---|
| Prepolymer NCO%: 6.0-6.4Grams Curene® 280 per 100 grams prepolymer: 39.3Rebound, %: 45Stoichiometry: 0.95Prepolymer Temperature, °F: 190-210Curene® 280 Temperature, °F: 158Post Cure Time, 212°F, hours: 16 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 107 | °C |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PBT-101G0 | Polymer Technology and Services, LLC | PBT | PTS |
| 4DUR® 9K34200 H | 4Plas | PBT | 4DUR® |
| Durethan® BKV 330 H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |
| KumhoSunny ABS 770SRS | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| I. Stern 1335 | I. STERN & CO. INC. | PP Homopolymer | I. Stern |