4POM® 10I30000
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4POM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vYxhb4_4POM-10I30000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4POM 10I30000 is a MFI 27 Unfilled POM |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 27 | g/10 min | ISO 1133 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.22 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2850 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 40 | % | ISO 527-2/5 |
| Flexural Modulus 2(23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Shear Strength | 54.9 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Tensile Impact Strength | 98.1 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 103 | °C | ISO 306/B |
| Melting Temperature 3 | 165 | °C | ISO 11357 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Heat Distortion | 158 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 80.0 - 100 | MPa | |
| Screw Speed | 300 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 30 - 50 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAFORM® 9 B AR | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| BJB Polyurethane TC-421 A/B-C CASTABLE | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Chemlon® JW21 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| KUBE PIR 21820 | KUBE Electronics AG | HDPE | KUBE PIR |
| LNP™ LUBRICOMP™ DL003 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |