LG ABS LG709W
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vYwtCB_LG-ABS-LG709W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Low Gloss, Heat Resistance Applications Automotive Interior Housing (Sun-Visor Mirror Cover Etc) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 43.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 15 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 69.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 59 | J/m | |
| -30°C, 6.40 mm | 49 | J/m | |
| 23°C, 3.20 mm | 160 | J/m | |
| 23°C, 6.40 mm | 140 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 114 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 106 | °C | |
| Vicat Softening Temperature | 114 | °C | ASTM D1525 5 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°) | 30 | ASTM D2457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.070 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 0.981 to 2.94 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Crastin® HR5315HFS NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Firepel® K130-LCS-00 | AOC, L.L.C. | Polyester Alloy | Firepel® |
| Polidan® PNT 0555/06 | Solvay Specialty Polymers | XLPE | Polidan® |
| KMI PP KM-008IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| Electrafil® 1105-10819 | Techmer Engineered Solutions | PEEK | Electrafil® |