Category: | Nylon 6 , Polyamide 6 |
Manufacturer: | Custom Resins Group |
Trademark: | Nylene® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | vYUgHz_Nylene-321-HS.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
|
General Information | |
---|---|
Additive |
|
Features |
|
Uses |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (23°C) | 55.2 | MPa | ASTM D638 |
Tensile Elongation (Break, 23°C) | 100 | % | ASTM D638 |
Flexural Modulus (23°C) | 1930 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 53.9 | °C | ASTM D648 |
Peak Melting Temperature | 216 | °C | ASTM D3418 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Ultramid® C3U BK23079 | BASF Corporation | Nylon 66/6 | Ultramid® |
VAMPAMID 66 2530 V0 P60 | Vamp Tech | Nylon 66 | VAMPAMID |
Karina WHITE PVC COMPOUND -E 855-10/150-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
Polyrocks EP8400X105F-1 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |
DAI-EL™ G-7401 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |