InnoGreen® BIO-90A
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoGreen® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vY0B7l_InnoGreen-BIO-90A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| InnoGreen® BIO-90A is a 90 shore A polyurethane elastomer formulated for hand-batch and vacuum assisted processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. InnoGreen® BIO-90A has been approved by the USDA as a bio preferred product. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.02 | g/cm³ | |
| Cured | 1.12 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 66 Mix Ratio by Volume: 42 | ||
| Demold Time | 180 to 540 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | 27 | % |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.10 | Pa·s | |
| 25°C 2 | 0.50 | Pa·s | |
| 25°C 3 | 0.50 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 14 to 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 85 to 95 | ASTM D2240 | |
| Tensile Strength | 13.8 | MPa | ASTM D638 |
| Tensile Elongation at Break | 65 | % | ASTM D638 |
| Tear Strength | 29.8 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN1721GB | Ginar Technology Co., LTD. | Nylon 66/6 | Mapex |
| RJM SI301G40 | RJM International, Inc. | PET | RJM |
| Sup-tech P9000 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Moplen HP741T | LyondellBasell Industries | PP Homopolymer | Moplen |
| Ketron® PEEK-CA30 | Quadrant Engineering Plastic Products | PEEK | Ketron® |