TUFNYL® RGF 10 BLUE
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SRF Ltd. |
| Trademark: | TUFNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vXr4qL_TUFNYL-RGF-10-BLUE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, 10% Glass fiber reinforced, Blue Pigmented material for injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | Internal Method |
| Water Absorption (Equilibrium) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 88 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 49.0 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K7009AH | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Utomer UT81P95A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| Geon™ Vinyl Flexible C80B1 WHITE 1473 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| K-vinyl 20 A 90 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| CALIBRE™ 303-4 | Sumika Styron Polycarbonate Limited | PC | CALIBRE™ |